信越LED Silicone Materials 产品选型表 |
|
Encapsulant SCR-Series |
|
产品名称 Product Name |
SCR-1011 |
SCR-1012 |
SCR-1016 |
|
A液粘度 Viscosity A side mPa s |
10,000 |
10,000 |
10,000 |
|
B液粘度 Viscosity B side mPa s |
50 |
1,000 |
50 |
|
混合粘度 Viscosity of mixed at 25℃ mPa s |
350 |
3,000 |
350 |
|
混合比 Mixing Ratio A:B |
100:100 |
100:100 |
100:100 |
|
标准固化条件 Standard cure condition |
70℃ 1h+150℃ 5h |
100℃ 1h+150℃ 5h |
|
折射率 Refractive Index |
1.52 |
1.50 |
1.52 |
|
硬度 Hardness Shore D |
70 |
75 |
70 |
|
玻璃转移点 Tg ℃ |
40 |
75 |
40 |
|
线膨胀系数 Linear expansion coefficient (a1) ppm |
70 |
72 |
70 |
|
线膨胀系数 Linear expansion coefficient (a2) ppm |
220 |
190 |
220 |
|
弹性模量 Modulus of elasticity MPa |
1,400 |
1,800 |
1,400 |
|
抗湾压力 Bending strength N/mm2 |
25 |
55 |
25 |
|
透光率 Light transmittance 400nm/2mm % |
88 |
88 |
88 |
|
Encapsulant KER-Series |
|
产品名称 Product Name |
KER-6000 |
KER-6050※ |
KER-6075 |
|
A液粘度 Viscosity A side mPa s |
4,400 |
4,100 |
20,000 |
|
B液粘度 Viscosity B side mPa s |
2,000 |
7,000 |
2,000 |
|
混合粘度 Viscosity of mixed at 25℃ mPa s |
2,800 |
5,000 |
7,500 |
|
混合比 Mixing Ratio A:B |
100:100 |
100:100 |
100:100 |
|
标准固化条件 Standard cure condition |
100℃ 1h+150℃ 5h |
|
折射率 Refractive Index |
1.51 |
1.51 |
1.44 |
|
硬度 Hardness Durometer A |
22 |
42 |
75 |
|
伸长率 Elongation % |
20 |
40 |
50 |
|
抗拉强度 Tensile strength MPa |
0.1 |
0.5 |
2.9 |
|
透光率 Light transmittance 400nm/ 2mm % |
89 |
87 |
90 |
|
Encapsulant KER-Series |
|
产品名称 Product Name |
KER-6100 |
|
A液粘度 Viscosity A side mPa s |
3,000 |
|
B液粘度 Viscosity B side mPa s |
2,000 |
|
混合粘度 Viscosity of mixed at 25℃ mPa s |
2,700 |
|
混合比 Mixing Ratio A:B |
100:5 |
|
标准固化条件 Standard cure condition |
100℃ 2h+150℃ 4h |
|
折射率 Refractive Index |
1.52 |
|
硬度 Hardness Durometer A |
55 |
|
玻璃转移点 Tg ℃ |
0 |
|
线膨胀系数 Linear expansion coefficient (a1) ppm |
70 |
|
线膨胀系数 Linear expansion coefficient (a2) ppm |
190 |
|
弹性模量 Modulus of elasticity MPa |
40 |
|
抗湾压力 Bending strength N/mm2 |
1.4 |
|
透光率 Light transmittance 400nm/2mm % |
88 |
|
Encapsulant KER-Series Methyl |
|
产品名称 Product Name |
KER-2500 |
KER-2600 |
X-32-2480-4 |
|
A液粘度 Viscosity A side mPa s |
8,300 |
6,500 |
7,800 |
|
B液粘度 Viscosity B side mPa s |
2,700 |
5,500 |
60 |
|
混合粘度 Viscosity of mixed at 25℃ mPa s |
4,300 |
6,000 |
NA |
|
混合比 Mixing Ratio A:B |
100:100 |
100:100 |
100:3 |
|
标准固化条件 Standard cure condition |
100℃ 2h+150℃ 5h |
|
折射率 Refractive Index |
1.41 |
1.41 |
1.42 |
|
硬度 Hardness Durometer A |
70 |
47 |
NA |
|
硬度 Hardness Shore D |
NA |
NA |
54 |
|
弹性模量 Modulus of elasticity MPa |
4.6 |
2.3 |
NA |
|
抗拉强度 Tensile strength MPa |
10 |
6 |
NA |
|
透光率 Light transmittance 400nm/2mm % |
90 |
92 |
91 |
|
Die-Bonging |
|
产品名称 Product Name |
KER-300-M2 |
KER-3100-U2 |
KER-3200-T1 |
SMP-2800L |
|
外观 Appearance |
透明 Translucent |
白色 White |
白色 White |
灰色 Gray |
|
粘度 Viscosity Pa s |
40 |
20 |
20 |
5 |
|
标准固化条件 Standard cure condition |
100℃ 1h+150℃ 2h |
150℃ 3h |
|
比重 Specific gravity |
1.13 |
2.04 |
2.54 |
3.1 |
|
硬度 Hardness Shore D |
56 |
70 |
71 |
NA |
|
厚度 Bond line thickness цm |
4 |
20 |
5 |
6 |
|
导热率 Thermal conductivity W/Mk |
0.2 |
0.6 |
0.6 |
1.0 |
|
热阻 Thermal resistance mm2K/W |
14.8 |
35.7 |
8.1 |
8.0 |
|
体积电阻率 Volume resistance Ω cm |
1.0 x 1016 |
NA |
NA |
3.2 x 10-5 |
|
类型 Binder polymer |
Methyl Silicone |
Methyl Silicone |
Methyl Silicone |
Polyimide Silicone |
|
溶剂 Solvent |
Non solvent |
Isoparaffin |
Isoparaffin |
Butyl carbitol acetate |
|
不挥发成分 Non volatile content % |
99 |
97 |
95 |
82 |
|
Potting |
|
产品名称 Product Name |
KE-1283A/B |
KE-1283A/B/C |
|
A液外观 Appearance A side |
黑色 Black |
黑色 Black |
|
B液外观 Appearance B side |
乳白色 Milky-White |
乳白色 Milky-White |
|
C剂外观 Appearance C side |
NA |
白色粉末 White Powder |
|
A液粘度 Viscosity A side at 25℃ Pa s |
2.8 |
2.8 |
|
B液粘度 Viscosity B side at 25℃ Pa s |
1.6 |
1.6 |
|
混合粘度 Viscosity of mixed 25℃ Pa s |
1.6 |
1.7 |
|
可操作时间 Pot Life at 23℃ hr |
5 |
5 |
|
混合比 Mixing ratio |
100：100 |
100：100：3 |
|
标准固化条件 Standard cure condition |
80℃ 2h |
80℃ 2h |
|
硬度 Hardness Asker C |
10 |
11 |
|
伸长率 Elongation % |
440 |
300 |
|
抗拉强度 Tensile strength MPa |
0.2 |
0.2 |
|
剪切粘接力（AI） Lap shear strength MPa |
0.16 |
0.14 |
|
剪切粘接力（PBT） MPa |
0.14 |
0.13 |
|
剪切粘接力（Polycarbonate） MPa |
0.17 |
0.18 |
|
阻燃性 Flame class UL94 |
V-1 |
V-1 |